CC41 |
CT41 |
|
(NP0)(C0G) |
(X7R) |
(X5R) |
(Y5Y) |
(Z5U) |
|
容量范围 |
0R5-104 |
181-225 |
153-107 |
103-226 |
682-275 |
|
温度系数 |
0±30ppm/℃
(-55℃—+125℃) |
±15%
(-55℃—+125℃) |
±15%
(-55℃—+85℃) |
+30%—-80%
(-25℃—+85℃) |
+22%—-56%
(+10℃—+85℃) |
|
绝缘电阻 |
1000MΩ-μF
或100GΩ
(100,000MΩ) |
1000MΩ-μF
或100GΩ
(100,000MΩ) |
100MΩ-μF或10G(≥16V)50MΩ-μF或10G(≤16V)(10,000MΩ) |
1000MΩ-μF
或100GΩ(10,000MΩ) |
|
介质强度 |
施加300%额定电压,1-5秒.充放电电流限制到50mA(最大)
注意:额定电压500V的产品施加150%额定电压 |
施加300%额定电压,1-5秒.充放电电流限制到50mA(最大) |
施加300%额定电压,1-5秒.充放电电流限制到50mA(最大)
注意:额定电压500V的产品施加150%额定电压 |
|
损耗
(tgδ) |
≤0.1%
1.0MHz C≤102 1.0KHz C＞102 |
≥50V ≤2.5%
25V ≤3.5%
16V ≤3.5%
≤10V ≤5.0% 1.0KHz
1.0Vrms C＞106
120Hz 0.5Vrms |
≥50V ≤2.5%
25V ≤5.0%
16V
C≤564 ≤5.0%
C＞564≤10.0% 1.0KHz
1.0Vrms C＞106
120Hz 0.5Vrms |
≥50V ≤5.0%
25V ≤7.0%
16V ≤9.0%
≤10V ≤12.5% 1.0KHz
1.0Vrms C＞106
120Hz 0.5Vrms |
100V ≤4.0%
50V ≤4.0%
25V ≤4.0%
1.0KHz 1.0Vrms
C＞106 120Hz 0.5Vrms |
|
容量误差 |
B=±0.1pF ＜10pF
C=±0.25pF＜10pF D=±0.50pF＜10pF
F=±1%≥10pF
G=±2%≥10pF J=±5%
K=±10% |
J=±5%
K=±10%
M=±20% |
K=±10%
M=±20% |
M=±20%
Z=-20—+80% |
M=±20%
Z=-20—+80% |
|
可焊性 |
EIA-198，方法301（245℃，5秒，Sn62焊料）在端头95%表面光滑 |
|
耐焊接热 |
EIA-198，方法302，条件B（
260℃，10秒）未滤去镍隔离层 |
|
负载寿命 |
EIA-198，方法201，1000小时，额定电压的200%，+125℃（X5R、Z5U和Y5V为+85℃）。（电气参数结果见下表） |
|
热冲击 |
|
EIA-198，方法202，条件B。第一步:-55℃（30±3分钟）；第二步:室温（≤3分钟）；第三步:+125℃（X7R、Y5V、Z5U为85℃）（30±3分钟）；第四步:室温（≤3分钟）。重复5次,在室温存放24±2小时后测试（电气参数：容量变化C0G：≤±2.5%或±0.25pF，取大者；X7R、X5R：≤±7.5%；Y5V、Z5U：≤±20%；其余参数满足初始值。） |
|
|
潮热试验 |
EIA-198，方法206。储存在85℃±2℃、相对湿度85%±5%1000小时（+48，0）施加额定电压。从试验箱取出后在室温下稳定24±2小时再测试（电气参数结果见下表） |