CC41 |
CT41 |
|
(NP0)(C0G) |
(X7R) |
(X5R) |
(Y5Y) |
(Z5U) |
|
容量範圍 |
0R5-104 |
181-225 |
153-107 |
103-226 |
682-275 |
|
溫度係數 |
0±30ppm/℃(-55℃—+125℃) |
±15%(-55℃—+125℃) |
±15%(-55℃—+85℃) |
+30%—-80%
(-25℃—+85℃) |
+22%—-56%(+10℃—+85℃) |
|
絕緣電阻 |
1000MΩ-μF
或100GΩ
(100,000MΩ) |
1000MΩ-μF或100GΩ
(100,000MΩ) |
100MΩ-μF或10G(≥16V)50MΩ-μF或10G(≤16V)(10,000MΩ) |
1000MΩ-μF或100GΩ(10,000MΩ) |
|
介質強度 |
施加300%額定電壓,1-5秒.充放電電流限制到50mA(最大)注意:額定電壓500V的產品施加150%額定電壓 |
施加300%額定電壓,1-5秒.充放電電流限制到50mA(最大) |
施加300%額定電壓,1-5秒.充放電電流限制到50mA(最大)注意:額定電壓500V的產品施加150%額定電壓 |
|
損耗
(tgδ)
|
≤0.1%
1.0MHz C≤102 1.0KHz C＞102 |
≥50V ≤2.5%
25V ≤3.5%
16V ≤3.5%
≤10V ≤5.0% 1.0KHz
1.0Vrms C＞106
120Hz 0.5Vrms |
≥50V ≤2.5%
25V ≤5.0%
16V
C≤564 ≤5.0%
C＞564≤10.0% 1.0KHz
1.0Vrms C＞106
120Hz 0.5Vrms |
≥50V ≤5.0%
25V ≤7.0%
16V ≤9.0%
≤10V ≤12.5%
1.0KHz 1.0Vrms
C＞106
120Hz 0.5Vrms |
100V ≤4.0%
50V ≤4.0%
25V ≤4.0%
1.0KHz 1.0Vrms
C＞106
120Hz 0.5Vrms |
|
容量誤差 |
B=±0.1pF ＜10pF
C=±0.25pF＜10pF D=±0.50pF＜10pF
F=±1%≥10pF
G=±2%≥10pF J=±5%
K=±10% |
J=±5%
K=±10%
M=±20% |
K=±10%
M=±20% |
M=±20%
Z=-20—+80% |
M=±20%
Z=-20—+80% |
|
可焊性 |
EIA-198，方法301（245℃，5秒，Sn62焊料）在端頭95%表面光滑 |
|
耐焊接熱 |
EIA-198，方法302，條件B（
260℃，10秒）未濾去鎳隔離層 |
|
負載壽命 |
EIA-198，方法201，1000小時，額定電壓的200%，+125℃（X5R、Z5U和Y5V為+85℃）。（電氣參數結果見下表） |
|
熱衝擊 |
|
IA-198，方法202，條件B。第一步:-55℃（30±3分鐘）；第二步:室溫（≤3分鐘）；第三步:+125℃（X7R、Y5V、Z5U為85℃）（30±3分鐘）；第四步:室溫（≤3分鐘）。重複5次,在室溫存放24±2小時後測試（電氣參數：容量變化C0G：≤±2.5%或±0.25pF，取大者；X7R、X5R：≤±7.5%；Y5V、Z5U：≤±20%；其餘參數滿足初始值。） |
|
|
潮熱試驗 |
EIA-198，方法206。儲存在85℃±2℃、相對濕度85%±5%1000小時（+48，0）施加額定電壓。從試驗箱取出後在室溫下穩定24±2小時再測試（電氣參數結果見下表 |